Structural characterization of post-consumption sludge as aggregates in construction materials

  • Giselle Carolina Barón-Gualdrón Universidad Industrial de Santander
  • Ángela Marcela Montaño-Angarita Universidad Industrial de Santander
  • Claudia Paulina Gonzalez-Cuervo Universidad Pontifica Bolivariana
  • Carlos Alberto Rios-Reyes Universidad Industrial de Santander
Palabras clave: DRX,Minerals,Mechanical resistance,SEM

Resumen

The present work covers the physical, mechanical and chemical characterization of pozzolanic materials. The pozzolans were obtained by mixing red clay, commercial bentonite and residual aluminous sludge, from a drinking water treatment plant. Ceramic cubes were manufactured, which were sintered at 1100 ° C and subsequently, were structurally characterized by DRX, SEM and EDS. Its compressive strength was also evaluated before and after being subjected to different environments. The results showed that the relations with which the standards for nonstructural bricks according to NTC 4017 (100 Kgf / cm2) are maintained are those that contain 10%, 20% and 30% of mud with respect to the clay maintaining an aggregate of bentonite 10% with resistances of 123.62 Kgf / cm2, 112.90 Kgf / cm2 and 107.32 Kgf / cm2, respectively. Likewise, for units exposed to corrosive environments, the 10% replacement mixture is the only one that meets the criteria established by the standard with a resistance of 112,80 Kgf/cm2 and in abrasive environments mixtures of 10% and 20% with resistance of 116,75 Kgf/cm2 and 101,96 Kgf/cm2 respectively.

 

Referencias

P. Torres, D. Hernández, and D. Paredes, “Uso productivo de lodos de plantas de tratamiento de agua potable en la fabricación de ladrillos cerámicos,” Rev. Ing. Constr., vol. 27, no. 3, pp. 145–154, 2012.

A. Seco et al., “Types of Wastes for the Production of Puzzolanic Materials - A Review,” in Industrial Waste, K.-Y. Show, Ed. INTECH, 2012, pp. 141–150.

L. Sandoval Yoval, L. Montellano Palacios, A. Martín Domínguez, L. Sánchez Guzmán, M. de L. Santana Ramírez, and M. Móran Plata, “Tratabilidad De Los Lodos Producidos En La Potabilización Del Agua,” 1989.

J. E. Perilla Sastoque, “Estrategias para el reusó de los lodos en la zona dos de la Empresa de Acueducto y alcantarillado de Bogotá y plantas de tratamiento de aguas potables y residuales,” Universidad Militar Nueva Granada, 2015.

D. Hernández, J. Villegas, J. Castaño, and D. Paredes, “Aprovechamiento De Lodos Aluminosos Generados En Sistemas De Potabilización, Mediante Su Incorporación Como Agregados En Materiales De Construcción,” Rev. Ing. Univ. Medellín, vol. 5, no. 8, pp. 119–132, 2006.

E. Galvis and K. Zambrano, “Identificación de las alternativas de uso ambiental de los lodos residuales de la planta de tratamiento de aguas la llana- campo 23, superintendencia la cira infantas, ECOPETROL,” Universidad Industrial de Santander, 2012.

J. A. Gutiérrez-Rosero, Á. I. Ramírez-Fajardo, R. Rivas, B. Linares, and D. Paredes, “Tratamiento de lodos generados en el proceso convencional de potabilización de agua,” Ing. Univ. Medellín, vol. 13, no. 25, pp. 13–27, 2014.

ICONTEC, “Métodos para muestreo y ensayos de unidades de mampostería y otros productos de arcilla,” in Norma Técnica Colombiana-4017, 2005, pp. 1–30.

ICONTEC, “Resistencia química de morteros,” in Norma Técnica Colombiana-489, 2005.

L. A. Ramírez Llamas, A. Jacobo Azuara, and J. M. Martínez Rosales, “Adsorción del naranja de metilo en solución acuosa sobre hidróxidos dobles laminares,” Acta Univ. is a Multidiscip. Sci. J., vol. 25, no. 3, pp. 25–34, 2015.

E. a F. Urquiza and L. M. Maspoch, “Estructura general de las arcillas utilizadas en la preparación de nanocompuestos poliméricos,” Ingenierias, vol. XII, no. 44, pp. 35–41, 2009.

E. Rocha, E. Armendariz, A. Rodriguez, and S. Esparza, Reforzamiento de cerámicos base alúmina con nanopartículas de titanio, no. Febrero. 2017.

Cómo citar
Barón-Gualdrón, G. C., Montaño-Angarita, Ángela M., Gonzalez-Cuervo, C. P., & Rios-Reyes, C. A. (2019). Structural characterization of post-consumption sludge as aggregates in construction materials. Respuestas, 24(1), 14-19. https://doi.org/10.22463/0122820X.1793

Descargas

La descarga de datos todavía no está disponible.
Publicado
2019-01-01
Sección
Artículos de Investigación